Fiberglass

Fiberglass

Strength & Thermal Stability

History
Fiberglass is produced into several forms and utilized in a vast array of composite and industrial applications. It is often used in thermoset and thermoplastic composite applications where the fiber is used as reinforcement. The mass production of glass fibers began in the 1930’s.

Composition
Large furnaces are used to melt silica sand, limestone, and various other minerals to liquid form. The liquid is then extruded through bushings and are coated (sized) to help bundle the filaments and prepare the fibers for composite resin interface. E-Glass typically is utilized for its high modulus properties as S-Glass has a higher breaking tenacity.

Connect with a Product Expert

IMPACT

  • Good tensile strength & modulus
  • Excellent thermal properties
  • Good chemical resistance
  • Good flame resistance
  • Good electrical insulation

Product bulletin: Fiberglass

Explore product information and technical properties

Fiber Selection Guide

Compare fiber properties and technical data

Fiber Conversion Calculator

Convert fiber measurements with this tool

Fiberglass Data
Resources
Property E-Glass S-Glass
Breaking Tenacity (g/d) 6.0-7.3 6.7-9.4
Specific Gravity (ratio) 2.58 2.48
Elongation at Break (%) 3.5 5.5
Tensile Modulus (g/d) 200-275 140-170
Equilibrium Moisture Regain at 55% RH (%) <0.03 <0.03
Creep at 40-48% ult tensile strength (%) 10.0-20.0 5.0-15.0
Shrinkage dry air 177 ̊ 30 mins (%) 0 0
Melt Point ( ̊C) 846 846
 
Fiber Selection Guide Product Selection Guide Compare fiber properties and technical data
Fiberglass Product/Service Overview Explore product information and technical properties